Rust-Oleum V2100 System Enamel aerosols are available in high-gloss, semi-gloss, flat, metallic and fluorescent finishes. They apply easily and dry fast to a tough, attractive corrosion-resistant finish featuring superior coverage, color, and gloss retention and resist chipping, cracking and peeling. They are available in a variety of colors including safety and fluorescent colors, and many match popular Rust-Oleum Industrial Enamel gallon colors for easy touch ups. Not for use on galvanized steel. Primer aerosols are used for maximum corrosion protection on clean, rusted or previously painted metal. Not for use on galvanized steel. They are fast dry, quick recoat rust inhibiting primers designed for use with the V2100 System Enamel aerosols to optimize corrosion control. Galvanizing aerosols are zinc-rich coatings that provide maximum corrosion resistance through galvanic protection. Use for touch-up and repair to damaged galvanized steel; production welds, galvanized ducts, storage tanks, fences, gutters, trucks, trailers, off-shore drilling rigs, utility towers, and more.
High Performance V2100 System Enamel complies with USDA FSIS regulatory sanitation performance standards for food establishment facilities.
SURFACE PREPARATION
Remove all dirt, grease, oil, salt and chemical contaminants by washing the surface with a commercial detergent, or other suitable cleaning method. Rinse with fresh water and allow to thoroughly dry. Remove loose paint and rust with a wire brush or sandpaper. Previously coated surfaces must be sound and in good condition. Smooth, hard, or glossy finishes should be scarified by sanding to create a surface profile.
STEEL: Hand tool (SSPC-SP-2) or power tool (SSPC-SP-3) clean to remove loose rust, mill scale, and deteriorated previous coatings. For best results, use Red Primer on sound rusted or clean metal before the application of a finish coat or intermediate primer.
PREVIOUSLY COATED: Previously coated surfaces must be sound and in good condition. Smooth, hard, or glossy finishes should be scarified by sanding to create a surface profile.
GALVANIZED STEEL: New galvanized steel may contain a surface wax or oil from the fabricator. This must be removed with Krud Kutter Original Cleaner/Degreaser, commercial detergent or other suitable cleaner. NOTE: Only the V2100 System Galvanizing Compounds are to be used on galvanized steel. Do not use any other of the V2100 System Primers or Finish Colors.
WEATHERED GALVANIZED STEEL: Remove loose rust and stains by hand tool (SSPC-SP-2) or power tool (SSPC-SP-3) prior to application of the Cold Galvanizing Compound.
APPLICATION
Use when temperature is above 50 F (10 C) and humidity is below 85% to ensure proper drying. Surface temperature must be between 50-100 F (10-38 C). Use primer on bare or rusted surfaces. Do not use any primer with V2116838 High Temperature Aluminum, V2176838 High Temperature Black, V2117838 Bright Galvanizing Compound or V2185838 Cold Galvanizing Compound. Protect surrounding surfaces from overspray. Overspray can carry a significant distance. Shake can for one minute after mixing ball is heard. Hold can 10-14 inches from surface. Apply several light coats a few minutes apart to avoid drips and runs.
DRY & RECOAT TIMES
Recoat within 1 hour or after 24 hours. Allow more time in cooler temperatures.
CLEAN-UP
Wipe off tip before storing. Clean-up wet paint with xylene or mineral spirits. Note: Clean-up wet V2115838 Silver Aluminum with xylol or acetone. Properly discard empty container. Do not burn or place in trash compactor. Empty container can be recycled.
CLOGGING
If the valve clogs, twist and pull off spray tip and rinse in a solvent such as mineral spirits. Do not insert any object into can valve opening.